Preparation and characterization of clean, single-crystalline YH<sub>x</sub> films (0≤x≤2.9) on W(110)
Auteur(s)
Hayoz, J.
Pillo, T.
Bovet, M.
Guthrie, St.
Pastore, G.
Schlapbach, Louis
Aebi, Philipp
Date de parution
2000
In
Journal of Vacuum Science & Technology A: Vacuum, Surfaces, and Films, American Vacuum Society, 2000/18/5/2417-2431
Résumé
Yttrium can be loaded with hydrogen up to high concentrations causing dramatic structural and electronic changes of the host lattice. We report on the preparation of clean, single-crystalline YH<sub>x</sub> films (0≤x≤2.9). The films have been characterized <i>in situ</i> combining angle-resolved photoelectron spectroscopy (ARPES) and low energy electron diffraction. Direct Y dihydride growth, i.e., Y evaporation under a H<sub>2</sub> partial pressures of ≈5×10<sup>–6</sup> mbar at 500 K on W(110), is the most convenient starting point for the preparation of clean single-crystalline Y hydride films covering H concentrations from the "clean metal" (x≈0) up to the lower boundary of the pure trihydride phase (x≈2.9). Upon annealing Y dihydride films the desired H concentration can be adjusted within the <sub>α</sub>-phase or the (<sub>α</sub>+<sup>β</sup>) two-phase regime. On the other hand, the extension of our photoelectron spectrometer with an homemade ultrahigh vacuum (UHV) compatible hydrogenation system allows to induce the transition from Y dihydride to Y trihydride within a few minutes. The hydrogenation system combines a high-pressure reaction cell with hydrogen permeation through a Pd–24%Ag tube. The overall design is such that the sample never gets in contact with non-UHV compartments. For direct Y dihydride growth on W(110) two equally populated face-centered- cubic(111) domains rotated by 180° with respect to each other are observed. In the <sub>α</sub>- and <sup>γ</sup>-phase the Y atoms form a hexagonal-close-packed(0001) oriented lattice. Furthermore, the previously established model for <i>in situ</i> H concentration estimation in Y [J. Hayoz et al., Phys. Rev. B <b>58</b>, R4270 (1998)] is extended successfully from the <sub>α</sub> to <sup>β</sup> to the to <sup>γ</sup>-phase transition. Ultraviolet photoemission spectroscopy data unequivocally reveal the opening of a gap extending as far as 1 eV below <i>E<sub>F</sub></i> for normal electron emission upon the phase-transformation from Y dihydride to Y trihydride. It also appears that the H absorption rate strongly depends on the H<sub>2</sub> purity. Our experimental results demonstrate the capability of this setup for <i>in situ</i> preparation and investigations on the geometrical and electronic structure of Y hydride films and, more generally, rare-earth hydride films using ARPES.
Identifiants
Type de publication
journal article
Dossier(s) à télécharger